Tempered Glass/Toughened Glass
Tempered glass is made by heating float glass to its softening point ( 650-700° C )and then suddenly cooling down to form compression in the surface layer of the glass, thus the mechanical strength is increased by 5 times. 

Features: 
1.5 times harder than ordinary float glass. 
2. Tensile strength for float glass 40 MPa (N/mm2), tempered glass, 120-200 MPa (N/mm2)
3. Quality standard AS/NZS 2208: 1996
4. It withstands abrupt temperature change of 220 Centigrade. 
5. Once breakage occurs, the glass disintegrates into small cubical fragments, which are relatively harmless to human body. 

Heat Strengthened Tempered Glass
1. Better flatness than tempered glass
2. Effectively resist the effect of thermal stress, avoid glass thermal explosion
3. Withstand a very wide range of rapid temperature changing with endurance of 200-300? C
4. Cooling rate lower and surface stress smaller than tempered glass

Use high quality raw clear glass.

Specification:
Flat Tempered Glass

MIN 90x90mm, Max 3660x2140mm
Thickenss 4mm, 5mm, 6mm, 8mm, 10mm, 12mm, 15mm, 19mm
Bent/Curved Tempered Glass
Max. Size 2200x750(mm)
Min Size 400*300(mm)
Thickness 5-19(mm)
Min. Benting Radius 370mm

Applications: 
1. External use of windows, doors, curtain wall, shopfronts, offices, houses, shops etc. 
2. Interior glass screens, partitions, balustrades etc. 
3. Shop display windows, showcases, display shelves etc. 
4. Furniture, table-tops, picture frames etc. 

Tempered Glass Equipments
1. Water jet machine, cutting tolerance +-0.1mm
2. Screen Printing Equipment
3. Single Straight-line Glass Edging Machine
4. Double Straight-line Glass Edging Machine
5. Round Glass Edging Machine
6. Glass Drilling Machine
7. Glass Tempering Furnace
8. Glass cutting line